Extreme structural stability of Ti0.5Sn0.5O2 nanoparticles: synergistic effect in the cationic sublattice
Résumé
Ti0.5Sn0.5O2 nanoparticles (∼5 nm and ∼10 nm) have been studied under high pressure by Raman spectroscopy. For particles with diameter ∼10 nm, a transformation has been observed at 20–25 GPa while for particles with ∼5 nm diameter no phase transition has been observed up to ∼30 GPa. The Ti0.5Sn0.5O2 solid solution shows an extended stability at the nanoscale, both of its cationic and anionic sublattices. This ultrastability originates from the contribution of Ti and Sn mixing: Sn stabilizes the cationic network at high pressure and Ti ensures a coupling between the cationic and anionic sublattices. This result questions a “traditional” crystallographic description based on polyhedra packing and this synergistic effect reported in this work is similar to the case of metamaterials but at the nanoscale.
Fichier principal
Machon2022.pdf (715.13 Ko)
Télécharger le fichier
Machon2022_supp.pdf (750.05 Ko)
Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Licence : CC BY NC - Paternité - Pas d'utilisation commerciale
Licence : CC BY NC - Paternité - Pas d'utilisation commerciale
Licence : CC BY - Paternité