The elasto-plastic nano- and microscale compressive behaviour of rehydrated mineralised collagen fibres

Résumé

Abstract The multiscale architectural design of bio-based nanostructured materials such as bone enables them to combine unique structure-mechanical properties that surpass classical engineering materials. In biological tissues, water as one of the main components plays an important role in the mechanical interplay, but its influence has not been quantified at the length scale of a mineralised collagen fibre. Here, we combine in situ experiments and a statistical constitutive model to identify the elasto-plastic micro- and nanomechanical fibre behaviour under rehydrated conditions. Micropillar compression and simultaneous synchrotron small angle X-ray scattering (SAXS) and X-ray diffraction (XRD) were used to quantify the interplay between fibre, mineralised collagen fibrils and mineral nanocrystals. Rehydration led to a 65% to 75% decrease of fibre yield stress and compressive strength, and a 70% decrease of stiffness with a 3x higher effect on stress than strain values. While in good agreement with bone extracellular matrix, the decrease is 1.5-3x higher compared to micro-indentation and macro-compression. Hydration has a higher influence on mineral than fibril strain while the highest difference to the macroscale was observed comparing mineral and tissue levels. Results suggest that the effect of hydration is strongly mediated by ultrastructural interfaces while corroborating the previously reported water-mediated structuring of bone apatite providing insights towards the mechanical consequences. Results show that the missing reinforcing capacity of surrounding tissue is more pronounced in wet than dry conditions when testing an excised array of fibrils, mainly related to the swelling of fibrils in the matrix. Differences leading to higher compressive strength between mineralised tissues do not seem to depend on the rehydration state while fibril mobilisation follows a similar regime in wet and dry conditions. The lack of kink bands point towards the role of water as an elastic embedding, thus, adapting the way energy is absorbed. Statement of significance Characterising structure-property-function relationships of biomaterials helps us to elucidate the underlying mechanisms that enables the unique properties of these architectured materials. Experimental and computational methods can advance our understanding towards their complex behaviour providing invaluable insights towards bio-inspired material development. In our study, we present a novel method for biomaterials characterisation. We close a gap of knowledge at the micro- and nanometre length scale by combining synchrotron experiments and a statistical model to describe the behaviour of a rehydrated single mineralised collagen fibre. Results suggest a high influence of hydration on structural interfaces, and the role of water as an elastic embedding. Using a statistical model, we are able to deduce the differences in wet and dry elasto-plastic properties of fibrils and fibres close to their natural hydration state.

Dates et versions

hal-03853398 , version 1 (15-11-2022)

Identifiants

Citer

Alexander Groetsch, Aurélien Gourrier, Daniele Casari, Jakob Schwiedrzik, Jonathan Shephard, et al.. The elasto-plastic nano- and microscale compressive behaviour of rehydrated mineralised collagen fibres. 2022. ⟨hal-03853398⟩

Collections

UGA CNRS LIPHY
10 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More