Masked stereolithography of hydroxyapatite bioceramic scaffolds

Résumé

This paper focuses on the tailoring of hydroxyapatite powders properties for the preparation of highly hydroxyapatite-loaded photocurable organic slurries. The suspensions were evaluated as feedstock for the production of hydroxyapatite scaffolds by stereolithography-based additive manufacturing technique. Then, a debinding-sintering process was designed to avoid the formation of cracks during the pyrolysis of the resin and sintering of the printed parts. A total porosity of 35 vol % and compression strength of 4.9 ± 0.3 MPa were obtained for the specimens printed at 45 • to the building platform. A slow degradation rate was observed due to the high degree of crystallinity and intrinsic stability of the hydroxyapatite phase. The tailoring of hydroxyapatite powders was required to lower the viscosity and increase the particle stability of the suspensions. The printed hydroxyapatite scaffolds showed promising results for surgery, in the case of minor or non-load bearing implants requiring slow resorption properties.
Fichier principal
Vignette du fichier
Open_Ceramics_9_100235_2022.pdf (11.25 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03844514 , version 1 (08-11-2022)

Identifiants

Citer

Pedro Navarrete-Segado, Mallorie Tourbin, Christine Frances, David Grossin. Masked stereolithography of hydroxyapatite bioceramic scaffolds: From powder tailoring to evaluation of 3D printed parts properties. Open Ceramics, 2022, 9, pp.100235. ⟨10.1016/j.oceram.2022.100235⟩. ⟨hal-03844514⟩
80 Consultations
43 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More