Titanium in GGBS-like calcium-magnesium-aluminosilicate glasses: Its role in the glass network, dissolution at alkaline pH and surface layer formation - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Non-Crystalline Solids Année : 2022

Titanium in GGBS-like calcium-magnesium-aluminosilicate glasses: Its role in the glass network, dissolution at alkaline pH and surface layer formation

Mathilde Poirier
Delphine Vantelon
Gautier Landrot
Jacques Schott
  • Fonction : Auteur
  • PersonId : 1127369

Résumé

Small TiO 2 contents in the slag-glass significantly reduce their cementitious reactivity. We investigated the role of Ti in the glass network and its influence on slag-glass dissolution. XANES and EPR analysis showed that 67% of Ti was present as Ti(IV) with about 70% in [5] Ti and 30% in [4] Ti coordination, and 33% as Ti(III). The presence of Ti had only a minor impact on initial dissolution rates at pH 11 (R ≈ 10 − 6 mol glass .s − 1 .m − 2). During dissolution, Ti accumulated in an amorphous layer at the glass-surface. Ti-coordination in this layer was 50% [5] Ti and 50% [6] Ti. At pH 11, the layer was mainly composed of TiO 2 (66 wt%), but intermixed with a hydrotalcite-like phase at pH 13. The loss of cementitious reactivity in the presence of Ti appears to be not only due to stabilization of the glass structure but also to the formation of a Ti-rich surface-layer, that may become passivating.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Publi_Ti_VF2-vm.pdf (2.01 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03820235 , version 1 (16-03-2023)

Identifiants

Citer

Simon Blotevogel, Mathilde Poirier, Delphine Vantelon, Erwan Chesneau, Charles-Emmanuel Dutoit, et al.. Titanium in GGBS-like calcium-magnesium-aluminosilicate glasses: Its role in the glass network, dissolution at alkaline pH and surface layer formation. Journal of Non-Crystalline Solids, 2022, 591, pp.121708. ⟨10.1016/j.jnoncrysol.2022.121708⟩. ⟨hal-03820235⟩
285 Consultations
121 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More