Manipulating refractive index, homogeneity and spectroscopy of Yb$^{3+}$-doped silica-core glass towards high-power large mode area photonic crystal fiber lasers
Résumé
Output power scaling of single mode large mode area (LMA) photonic crystal fiber (PCF) amplifiers urgently requires the low refractive index of Yb 3+-doped silica glasses whilst maintaining high optical homogeneity. In this paper, we report on a promising alternative Yb 3+ /Al 3+ /F-/P 5+-co-doped silica core-glass (YAFP), which is prepared by modified sol-gel method developed by our group and highly suitable for fabricating high power LMA PCF amplifiers. By controlling the doping combinations of Al 3+ /F-/P 5+ in Yb 3+doped silica glass,it not only ensures low refractive index (RI) but also maintains the excellent optical homogeneity and spectroscopic properties of Yb 3+. The spectroscopic properties of Yb 3+ ions have not deteriorated by the co-doping of Fand P 5+ in YAFP glass compared with that of Yb 3+ /Al 3+ co-doped silica glass. A large-size (⌀5 mm × 90 mm) YAFP silica-core glass rod with low average RI difference of 2.6 × 10 −4 (with respect to pure silica glass), and low radial and axial RI fluctuations of ~2 × 10 −4 , was prepared. A LMA PCF with 50 µm core diameter was obtained by stack-capillary-draw techniques using YAFP core glass. Its core NA is 0.027. An average amplified power of 97 W peaking at 1030 nm and light-light efficiency of 54% are achieved from a 6.5 m long PCF in the pulse amplification laser experiment. Meanwhile, quasi-single-mode transmission is obtained with laser beam quality factor M 2 of 1.4.
Origine | Fichiers éditeurs autorisés sur une archive ouverte |
---|