Phase diagram and order-disorder transitions in Y0.9Gd0.1Fe2Hx hydrides (x ≥ 2.9) - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Alloys and Compounds Année : 2022

Phase diagram and order-disorder transitions in Y0.9Gd0.1Fe2Hx hydrides (x ≥ 2.9)

Résumé

Y0.9Gd0.1Fe2, which crystallize in a C15 cubic structure, can absorb up to 5 H/f.u. and its pressure-compo sition isotherm displays a multiplateau behavior related to the existence of several hydrides with different crystal structures. At room temperature Y0.9Gd0.1Fe2Hx hydrides (2.9 ≤ x ≤ 5) crystallize in three phases with cubic structure (C1, C2 and C3), two phases with monoclinic structures (M1 and M2), and one phase with orthorhombic structure (O), with the following sequence for increasing H concentration: C1, M1, C2, M2, C3, O. Each phase exists as single phase within a H homogeneity range, and they are separated from each other by two-phase domains. The reductions of crystal symmetry are related to various hydrogen orders into interstitial sites. Weak superstructure peaks were indexed by doubling the cubic cell parameter of the cubic C2 phase. Upon heating, the monoclinic M1 and M2 and the cubic C2 phases undergo order-disorder (O-D) transitions toward a disordered cubic structure CDis. These O-D transitions are reversible with thermal hysteresis effects. The cubic C3 and orthorhombic O phases transform into a disordered cubic phase companied by H desorption.
Fichier principal
Vignette du fichier
Article-Y09GD01FE2HX-OD-transition-14-11-21.pdf (1.14 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03796082 , version 1 (04-10-2022)

Identifiants

Citer

Valérie Paul-Boncour, Karine Provost, Eric Alleno, Adama N’Diaye, Fabrice Couturas, et al.. Phase diagram and order-disorder transitions in Y0.9Gd0.1Fe2Hx hydrides (x ≥ 2.9). Journal of Alloys and Compounds, 2022, 896, pp.163016. ⟨10.1016/j.jallcom.2021.163016⟩. ⟨hal-03796082⟩
8 Consultations
14 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More