Highly luminescent and photostable core/shell/shell ZnSeS/Cu:ZnS/ZnS quantum dots prepared via a wild aqueous route - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Nanomaterials Année : 2022

Highly luminescent and photostable core/shell/shell ZnSeS/Cu:ZnS/ZnS quantum dots prepared via a wild aqueous route

Résumé

An aqueous-phase synthesis of 3-mercaptopropionic acid (3-MPA)-capped core/shell/shell ZnSeS/Cu:ZnS/ZnS QDs was developed. The influence of the Cu-dopant location on the photoluminescence (PL) emission intensity was investigated, and the results show that the introduction of the Cu dopant in the first ZnS shell leads to QDs exhibiting the highest PL quantum yield (25%). The influence of the Cu-loading in the dots on the PL emission was also studied, and a shift from blue-green to green was observed with the increase of the Cu doping from 1.25 to 7.5%. ZnSeS/Cu:ZnS/ZnS QDs exhibit an average diameter of 2.1 ± 0.3 nm and are stable for weeks in aqueous solution. Moreover, the dots were found to be photostable under the continuous illumination of an Hg-Xe lamp and in the presence of oxygen, indicating their high potential for applications such as sensing or bio-imaging.
Fichier principal
Vignette du fichier
nanomaterials-12-03254.pdf (1.2 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03780644 , version 1 (19-09-2022)

Licence

Paternité

Identifiants

Citer

Salima Mabrouk, Hervé Rinnert, Lavinia Balan, Jordane Jasniewski, Sébastien Blanchard, et al.. Highly luminescent and photostable core/shell/shell ZnSeS/Cu:ZnS/ZnS quantum dots prepared via a wild aqueous route. Nanomaterials, 2022, 12, pp.3254. ⟨10.3390/nano12183254⟩. ⟨hal-03780644⟩
63 Consultations
23 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More