Mechanical and macromolecular changes during thermal degradation of polyphenylsulfone

Abstract

Polyphenylsulfone was thermally aged at temperatures corresponding to its processing and was mainly shown to undergo crosslinking as observed by measurements of average molar mass, rheometry and changes in glass transition temperature. Those experiments were completed by mechanical testing thin sample films at 250 and 280 °C. The same degradation mechanisms were observed and result in a strong decrease of ultimate strain accompanied by a slight decrease in elastic modulus and yield stress. Overall results were discussed using well know structure-properties relationships.
Fichier principal
Vignette du fichier
PIMM_PDS_2022_LEBERT.pdf (1.98 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03719466 , version 1 (11-07-2022)

Identifiers

Cite

Nicolas Lebert, Nicolas Gay, Emmanuel Richaud. Mechanical and macromolecular changes during thermal degradation of polyphenylsulfone. Polymer Degradation and Stability, 2022, 195, pp.109812. ⟨10.1016/j.polymdegradstab.2021.109812⟩. ⟨hal-03719466⟩
44 View
114 Download

Altmetric

Share

Gmail Facebook X LinkedIn More