Successive steps of growth of compacted graphite in cast irons

Résumé

Holding during 8 hours a melt prepared for casting SGI leads to fading of the spheroidizing treatment and thus to growth of compacted graphite instead of spheroidal graphite. Such a melt was cast in thermal analysis cups at 25-30 minutes interval without inoculation. It solidified first in the stable system and more and more in the metastable system. Accordingly, recalescence first increased as more of compacted graphite solidified, but then decreased when more and more of the solidification occurred in the metastable system. Comparison of the results of the present study with those of a previous similar series showed a higher peak recalescence while the number of compacted graphite cells and the graphite fraction were the same within experimental scattering. Furthermore, as the amount of spheroidizers was similar in both series, there is no clear reason for this difference in recalescence, which should be investigated further.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Sertucha_2022.pdf (2.9 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03689079 , version 1 (19-07-2022)

Identifiants

Citer

Jon Sertucha, Jacques Lacaze, Anna Regordosa, Urko de La Torre. Successive steps of growth of compacted graphite in cast irons. Tecnologia em Metalurgia, Materiais e Mineração, 2022, 19, pp.e2620. ⟨10.4322/2176-1523.20222620⟩. ⟨hal-03689079⟩
39 Consultations
34 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More