Silver as Anode in Cryolite—Alumina-Based Melts
Résumé
The anodic behaviour of silver was investigated in cryolite—alumina-based melt. Silver has a lower melting point (ca. 960◦C) than the other metals considered as possible inert materials for aluminium electrolysis. The working temperature used in aluminium industry is approximately 960◦C, depending on the melt composition. Therefore, the stability of silver during the anodic process was tested at 870◦C in an acidic electrolyte consisting of 65.5 mass % Na3AlF6 + 22.9 mass % AlF3 + 5.7 mass % CaF2 + 3.9 mass % LiF + 2 mass % Al2O3 with the melting point ca. 850◦C. The electrolyte without alumina was prepared as well, with the melting point ca. 860◦C. The resulting cryolite ratio (CR = n(NaF)/n(AlF3)) for both electrolytes was equal to 1.6. The behaviour of the silver anode was studied by voltammetry measurements. The electrochemical study showed that an oxidation reaction occurred at a potential below the oxygen evolution potential. Silver was not found to be stable under oxygen evolution. The degradation of the silver anode was apparent after electrolysis.
Domaines
Génie chimiqueOrigine | Fichiers produits par l'(les) auteur(s) |
---|