Silicon electrodeposition in molten fluorides

Résumé

Silicon nucleation process was investigated in molten NaF-KF (40-60 mol%) on silver electrodes in the 820-950°C temperature range in order to optimize silicon coating operating conditions. Chronoamperometric measurements evidenced that silicon electrodeposition process involved an instantaneous nucleation with diffusion-controlled nuclei growth whatever temperature and Si(IV) ions concentration in the mixture. The overpotential and temperature influence on nucleation sites number was also studied. Silicon deposits were obtained using the same temperature range as nucleation study, for different current densities on substrates: Ni, Ag, Cgraphite and Cvitreous. A sensitive influence of the cathodic substrate on the deposit adherence and roughness was observed and discussed.
Fichier principal
Vignette du fichier
8619_Massot.pdf (762.99 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03537607 , version 1 (20-01-2022)

Identifiants

Citer

Anne-Laure Bieber, Laurent Massot, Mathieu Gibilaro, Laurent Cassayre, Pierre Taxil, et al.. Silicon electrodeposition in molten fluorides. Electrochimica Acta, 2011, 62, pp.282-289. ⟨10.1016/j.electacta.2011.12.039⟩. ⟨hal-03537607⟩
16 Consultations
18 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More