Investigation of N2 plasma GaAs surface passivation efficiency against air exposure: towards an enhanced diode - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Applied Surface Science Année : 2022

Investigation of N2 plasma GaAs surface passivation efficiency against air exposure: towards an enhanced diode

Hussein Mehdi
François Réveret
Christine Robert-Goumet
Luc Bideux
Bernard Gruzza
  • Fonction : Auteur
Philip Eric Hoggan
Joël Leymarie
  • Fonction : Auteur
  • PersonId : 835166
Yamina Andre
Evelyne Gil
Guillaume Monier

Résumé

GaAs(001) substrates nitrided with N 2 plasma at various temperatures were investigated after being exposed to air for 40 days. They were studied by means of parallel angle-resolved X-ray photoelectron spectroscopy, scanning electron microscopy, micro-photoluminescence and time-resolved photoluminescence (TRPL). Several nitrided GaAs Schottky diodes were manufactured to find the optimal nitridation conditions for high diode quality. An improvement on the ideality factor was achieved for a diode with 1.3 nm-thick GaN layer grown at room temperature and crystallized at 620 °C. The crystallization process was needed to enhance the air-exposed GaAs photoluminescence efficiency by a factor 15. TRPL measurements showed a spectacular increase in the decay time (×4), even for a sample exposed to air for 2 years. A high level of GaAs surface chemical protection was achieved. Indeed, neither the element arsenic As 0 nor Ga and As oxides states were detected at the GaN/GaAs interface for nitridation at high temperature (500 °C), yielding a 3.1 nm-thick GaN layer. However, for nitridation temperatures above 300 °C, pits with an inversed pyramidal shape and square base were formed at the surface, their size increased as nitridation temperature was raised. These pits acted as non-recombination centers which reduced the GaAs photoluminescence yield.
Fichier principal
Vignette du fichier
Article revise sans marque.pdf (1.2 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03515255 , version 1 (06-01-2022)

Identifiants

Citer

Hussein Mehdi, François Réveret, Christine Robert-Goumet, Luc Bideux, Bernard Gruzza, et al.. Investigation of N2 plasma GaAs surface passivation efficiency against air exposure: towards an enhanced diode. Applied Surface Science, 2022, 579, pp.152191. ⟨10.1016/j.apsusc.2021.152191⟩. ⟨hal-03515255⟩
90 Consultations
167 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More