3D crack growth monitoring in wood-based materials by means of X-ray computed microtomography and 2D DIC analysis method

Seif Hamdi
  • Fonction : Auteur
Pitti, Rostand Moutou
  • Fonction : Auteur
Mohamed Teguedi
  • Fonction : Auteur
Bernard Odounga
  • Fonction : Auteur
Benoit Blaysat
  • Fonction : Auteur

Résumé

Crack initiation and growth in wood-based materials, commonly employed in buildings and civil engineering structures, still generate considerable inspection and repair costs besides the fact that is one of the most important factors involved in structural failure. X-ray computed microtomography (X-ray CT), which provides 3D images with a high level of detail at both the micro- and macro-scales, is frequently used as a non-destructive technique. In this work, the propagation of a 20 mm initial crack in Mixed-Mode Crack Growth (MMCG) wood samples was tracked using high-energy X-ray CT. Crack growth data were then determined from 3D tomography reconstructions. 2D crack tracking data measurements from fracture surface were performed using 2D Digital Image Correlation (DIC) analysis method. The collected 3D measurements were compared to those obtained from 2D DIC analysis and conventional mechanical tests in order to measure long and small crack growth. The observed results demonstrates that X-ray CT and surface tracking analysis usingDICgrid methodcan be successfully combined to study the crack propagation

Fichier principal
Vignette du fichier
bitstream_124506.pdf (912 Ko) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte
Licence

Dates et versions

hal-03465391 , version 1 (03-12-2021)

Licence

Identifiants

  • HAL Id : hal-03465391 , version 1

Citer

Seif Hamdi, Pitti, Rostand Moutou, Mohamed Teguedi, Bernard Odounga, Benoit Blaysat. 3D crack growth monitoring in wood-based materials by means of X-ray computed microtomography and 2D DIC analysis method. CFM 2017 - 23ème Congrès Français de Mécanique, Aug 2017, Lille, France. ⟨hal-03465391⟩

Collections

51 Consultations
64 Téléchargements

Partager

  • More