The role of mixed alkali metal cations on the formation of nanosized CHA zeolite from colloidal precursor suspension

Résumé

A clear understanding of the crystal formation pathways of zeolites remains one of the most challenging issues to date. Here we investigate the synthesis of nanosized chabazite (CHA) zeolites using organic template-free colloidal suspensions by varying the time of aging at room temperature and the time of hydrothermal treatment at 90 °C. The role of mixed alkali metal cations (Na+, K+, Cs+) on the formation of CHA in the colloidal suspensions was studied. Increasing the aging time of the precursor colloidal suspension from 4 to 17 days resulted in faster crystallization of CHA nanocrystals (3 h instead of 7 h at 90 °C) to afford significantly smaller particles (60 nm vs 600 nm). During the crystallization a considerable change in the content of inorganic cations in the recovered solid material was observed to coincide with the formation of the CHA nanocrystals. The Na+ cations were found to direct the formation of condensed and pre-shaped aluminosilicate particles in the colloidal precursor suspensions, while K+ cations facilitated the formation of secondary building units (SBUs) of the CHA type framework structure such as d6r and cha cages, and the Cs+ cations promoted the long-range crystalline order facilitating the crystallization of stable zeolite nanocrystals
Fichier principal
Vignette du fichier
Synthesis of nanosized CHA framework structure.pdf (1.63 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03414919 , version 1 (04-11-2021)

Identifiants

Citer

Sajjad Ghojavand, Edwin B Clatworthy, Aurélie Vicente, Eddy Dib, Valérie Ruaux, et al.. The role of mixed alkali metal cations on the formation of nanosized CHA zeolite from colloidal precursor suspension. Journal of Colloid and Interface Science, 2021, 604, pp.350-357. ⟨10.1016/j.jcis.2021.06.176⟩. ⟨hal-03414919⟩
106 Consultations
139 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More