Исследование фотокаталитической антимикробной активности нанокомпозитов на основе TiO2-Al2O3 при воздействии светодиодного излучения (405 nm) на стафилококки
Résumé
The photocatalytic activity of nanocomposites based on theta-modification of aluminum oxide Al2O3 with different TiO2 content for heterogeneous photocatalysis and biodegradation of pathogenic microorganisms under the action of LED radiation with a wavelength of 405 nm has been studied. It was found that all the investigated nanocomposites have photocatalytic activity. The maximum antibacterial efficiency of composites with a TiO2 content of 8 wt% (reduction of CFU of Staphylococcus aureus 209 P to 86%), which allows us to recommend this nanomaterial as a promising antimicrobial coating.
Исследована фотокаталитическая активность нанокомпозитов на основе theta-модификации оксида алюминия Al 2 O 3 с различным содержанием TiO 2 для гетерогенного фотокатализа и биодеструкции патогенных микроорганизмов при воздействии светодиодного излучения с длиной волны 405 nm. Установлено, что все исследованные нанокомпозиты обладают фотокаталитической активностью. Максимальна антибактериальная эффективность композитов с содержанием TiO 2 8 wt.% (снижение CFU Staphylococcus aureus 209 P до 86%), что позволяет рекомендовать этот наноматериал в качестве перспективного антимикробного покрытия. Ключевые слова: фотокаталитическое воздействие, theta-модификация Al 2 O 3 , TiO 2 , СИД излучение (405 nm), антибактериальная эффективность, Staphylococcus aureus 209 P.
Domaines
Matériaux| Origine | Fichiers produits par l'(les) auteur(s) |
|---|