Flash Spark Plasma Sintering of 3YSZ: Modified sintering pathway and impact on grain boundary formation

Résumé

Yttria stabilized zirconia (3 mol% YSZ) ceramics were prepared by Flash-SPS, while allowing high heating rates up to 200°C/s, which led to the extremely fast densification within a few seconds. The high heating rates had strong impact on sintering mechanisms, in terms of densification and grain growth. While the specimens ended with 5 to 15 vol% porosity and limited grain growth (< 350 nm), their hardness is higher than fully dense counterpart SPSed ceramics. Using the sintering trajectories, microstructural observations, and impedance spectroscopy, we highlight altered sintering mechanism which resulted in very thin grain boundaries compared to SPS. It appears that densification is largely advanced at grain boundary interfaces, with no residual nano-pores at the grain junctions, where some pores with size comparable to grain size were present. This opens up opportunities for the fabrication of porous lightweight ceramics with good mechanical properties.

Domaines

Matériaux
Fichier principal
Vignette du fichier
2021-125.pdf (1.6 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03373353 , version 1 (11-10-2021)

Identifiants

Citer

Thomas Hérisson de Beauvoir, Zakaria Ghomari, Geoffroy Chevallier, Andréas Flaureau, Alicia Weibel, et al.. Flash Spark Plasma Sintering of 3YSZ: Modified sintering pathway and impact on grain boundary formation. Journal of the European Ceramic Society, 2021, 41 (15), pp.7762-7770. ⟨10.1016/j.jeurceramsoc.2021.08.013⟩. ⟨hal-03373353⟩
40 Consultations
59 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More