Magnetic transitions with magnetocaloric effects near room temperature related to structural transitions in Y0.9Pr0.1Fe2D3.5 deuteride - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Applied Physics Année : 2021

Magnetic transitions with magnetocaloric effects near room temperature related to structural transitions in Y0.9Pr0.1Fe2D3.5 deuteride

A. Herrero
E. Elkaim

Résumé

The structural and magnetic properties of Y0.9Pr0.1Fe2D3.5 deuteride have been investigated by synchrotron and neutron diffraction, magnetic measurements, and differential scanning calorimetry. Deuterium insertion induces a 23.5 % cell volume increase and a lowering of crystal symmetry compared to the cubic C15 Y0.9Pr0.1Fe2 parent compound (Fd-3m SG). The deuteride is monoclinic (P21/c SG) below 330 K and undergoes a first order transition between 330 and 350 K towards a pseudo-cubic structure (R-3m SG) with TO-D = 342(2) K. I In both structures the D atoms are located in 96 % R2Fe2 and 4 % RFe3 tetrahedral interstitial sites (R=Y0.9Pr0.1). The compound is ferromagnetic, accompanied by a magnetostrictive effect below TC = 274 K. The analysis of the critical exponents indicates a second order type transition with a deviation from the isotropic 3D Heisenberg model towards the 3D XY model. This implies an easy plane of magnetization in agreement with cell parameter variation showing a planar magnetic orientation. A weak magnetic peak is even observed at the order-disorder transition with a maximum at 343 K. Magnetic entropy variations are characteristic of direct and inverse magnetocaloric effects at TC and TO-D respectively.
Fichier principal
Vignette du fichier
Publi-JAP-version-HAL.pdf (1.58 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03367633 , version 1 (06-10-2021)

Licence

Paternité

Identifiants

Citer

Valérie Paul‐boncour, A. Herrero, V. Shtender, K. Provost, E. Elkaim. Magnetic transitions with magnetocaloric effects near room temperature related to structural transitions in Y0.9Pr0.1Fe2D3.5 deuteride. Journal of Applied Physics, 2021, 130 (11), pp.113904. ⟨10.1063/5.0061200⟩. ⟨hal-03367633⟩
7 Consultations
66 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More