Nanomechanical properties of nanoconfined polystyrene nanoparticles in nanoblends

Yahya Rharbi
  • Fonction : Auteur
M. Yousfi

Résumé

The role of nanoconfinement on the glass transition temperature (Tg) of polymers has been extensively studied in the thin film geometry. This work looks at the Tg of nanoconfined polystyrene in spherical nanoparticles (27- 200 nm), individually dispersed in crosslinked polybuthylmethacrylate matrices. A reduction of Tg compared to the bulk was observed in PS nanospheres via neutron scattering-mechanical tests and was found to decrease with decreasing diameter for D< 50nm. The general trend of Tg depression in nanospheres was found to be similar to the results on thin film geometry.
Fichier principal
Vignette du fichier
bitstream_22696.pdf (382.15 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03362466 , version 1 (01-10-2021)

Identifiants

  • HAL Id : hal-03362466 , version 1

Citer

Yahya Rharbi, M. Yousfi. Nanomechanical properties of nanoconfined polystyrene nanoparticles in nanoblends. CFM 2007 - 18ème Congrès Français de Mécanique, Aug 2007, Grenoble, France. ⟨hal-03362466⟩

Collections

CFM2007
5 Consultations
3 Téléchargements

Partager

Gmail Facebook X LinkedIn More