Ultra-low thermal conductivity in scheelite and A-deficient scheelite ceramics

Résumé

Synthesis of scheelite-type oxides based on lanthanum and barium molybdate (BaMoO4 and La2Mo3O12 ceramics) were successfully prepared via conventional solid-state reaction method. Dense ceramics were obtained by conventional sintering. Structural, microstructural and thermal properties of both sintered ceramics were assessed to identify the impact of cation deficiency on thermal conductivity. BaMoO ceramic has shown a decrease in thermal conductivity from 0.8 W m-1 K-1 to 0.65 W m-1 K-1 from 400 K to 650 K. The deficient scheelite La Mo O compound was found to further reduce thermal conductivity. An ultra-low thermal conductivity constant value of about 0.59-0.62 W m-1 K-1 was calculated over the entire temperature range. This value is the lowest recorded value for oxides so far discovered and such materials may be promising ones for thermal insulating applications
Fichier principal
Vignette du fichier
S135964622100230X.pdf (957.17 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03221343 , version 1 (09-05-2023)

Licence

Copyright (Tous droits réservés)

Identifiants

Citer

Eliane Bsaibess, Fabian Delorme, Isabelle Monot-Laffez, Fabien Giovannelli. Ultra-low thermal conductivity in scheelite and A-deficient scheelite ceramics. Scripta Materialia, 2021, 201, pp.113950. ⟨10.1016/j.scriptamat.2021.113950⟩. ⟨hal-03221343⟩
82 Consultations
9 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More