CuO photoelectrodes synthesized by the sol-gel method for water splitting

Résumé

CuO is an attractive photocatalytic material for water splitting due to its high earth abundance and low cost. In this paper, we report the deposition of CuO thin films by sol–gel dip-coating process. Sol deposition has attractive advantages including low-cost solution processing and uniform film formation over large areas with a fairly good control of the film stoichiometry and thickness. Pure CuO phase was obtained for calcination temperatures higher than 360 °C in air. The CuO photocurrents for hydrogen evolution depend on the crystallinity and the microstructure of the film. Values of −0.94 mA cm−2 at pH = 8 and 0 V vs. RHE were achieved for CuO photoelectrodes annealed at 400 °C under air. More interestingly, the stability of the photoelectrode was enhanced upon the sol–gel deposition of a TiO2 protective layer. In this all sol–gel CuO/TiO2 photocathode, a photocurrent of −0.5 mA cm−2 is achieved at pH = 7 and 0 V vs. RHE with a stability of ~100% over 600 s.
Fichier principal
Vignette du fichier
Toupin_JSST_final_text.pdf (1.32 Mo) Télécharger le fichier
Toupin_JSST_Electronic supplementary material.pdf (577.37 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03181628 , version 1 (18-10-2022)

Identifiants

Citer

J. Toupin, H. Strubb, S. Kressmann, V. Artero, N. Krins, et al.. CuO photoelectrodes synthesized by the sol-gel method for water splitting. Journal of Sol-Gel Science and Technology, 2019, 89 (1), pp.255-263. ⟨10.1007/s10971-018-4896-3⟩. ⟨hal-03181628⟩
111 Consultations
240 Téléchargements

Altmetric

Partager

More