Microstructure and Mechanical Properties of AA7075 Aluminum Alloy Fabricated by Spark Plasma Sintering (SPS)

Résumé

AA7075 aluminum alloy is widely used for several high-technology applications for its high mechanical strength to weight ratio but is still the subject of several studies seeking a further increase in its mechanical properties. A commercial powder is used, either as-received or after ball-milling. Dense AA7075 samples are prepared in one step by Spark Plasma Sintering, at 550 °C with a holding time of 15 min and a uniaxial pressure of 100 MPa. No additional heat treatment is performed. Laser granulometry, X-ray diffraction and optical- and scanning electron microscopy show that both grain size and morphology are preserved in the dense samples, due to the relatively low temperature and short sintering time used. The samples prepared using the ball-milled powder exhibit both higher Vickers microhardness and transverse fracture strength values than those prepared using the raw powder, reflecting the finer microstructure.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Soares_27348.pdf (1.9 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03134717 , version 1 (08-02-2021)

Identifiants

Citer

Elder Soares, Nadège Bouchonneau, Elizeth Alves, Kleber Alves, Oscar Araújo Filho, et al.. Microstructure and Mechanical Properties of AA7075 Aluminum Alloy Fabricated by Spark Plasma Sintering (SPS). Materials, 2021, 14 (2), pp.430. ⟨10.3390/ma14020430⟩. ⟨hal-03134717⟩
48 Consultations
156 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More