Combined XPS / TEM study of the chemical composition and structure of the passive film formed on additive manufactured 17-4PH stainless steel - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Surfaces and Interfaces Année : 2021

Combined XPS / TEM study of the chemical composition and structure of the passive film formed on additive manufactured 17-4PH stainless steel

Résumé

he structure and chemical composition of the passive film formed on 17-4PH martensitic stainless steel (MSS) manufactured by powder bed laser beam melting (LBM) were investigated combining XPS and TEM analyses, by comparison to a conventional l 7-4PH. The structure of the passive film was found similar for both MSSs, with, on the matrix, a duplex layer composed of Fe and Cr oxy-hydroxide followed by an intermediate layer enriched in metallic compounds. A particular Nb oxide film formed on the NbC precipitates merging to the surface for both MSSs. Significant differences in thickness and Cr distribution were observed between both MSSs.

Domaines

Matériaux
Fichier principal
Vignette du fichier
BARROUX_27239.pdf (4.13 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03111555 , version 1 (15-01-2021)

Identifiants

Citer

Adrien Barroux, Thomas Duguet, Nadège Ducommun, Eric Nivet, Julien Delgado, et al.. Combined XPS / TEM study of the chemical composition and structure of the passive film formed on additive manufactured 17-4PH stainless steel. Surfaces and Interfaces, 2021, 22, pp.100874. ⟨10.1016/j.surfin.2020.100874⟩. ⟨hal-03111555⟩
52 Consultations
23 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More