Quantitative ultrasound assessment of the influence of roughness and healing time on osseointegration phenomena

Résumé

The evolution of bone tissue quantity and quality in contact with the surface of orthopedic and dental implants is a strong determinant of the surgical outcome but remains difficult to be assessed quantitatively. The aim of this study was to investigate the performance of a quantitative ultrasound (QUS) method to measure bone-implant interface (BII) properties. A dedicated animal model considering coin-shaped titanium implants with two levels of surface roughness (smooth, Sa = 0.49 µm and rough, Sa = 3.5 µm) allowed to work with a reproducible geometry and a planar interface. The implants were inserted in rabbit femurs and tibiae for 7 or 13 weeks. The ultrasonic response of the BII was measured ex vivo, leading to the determination of the 2-D spatial variations of bone in contact with the implant surface. Histological analysis was carried out to determine the bone-implant contact (BIC) ratio. The amplitude of the echo was significantly higher after 7 weeks of healing time compared to 13 weeks, for both smooth (p < 0.01) and rough (p < 0.05) implants. A negative correlation (R = − 0.63) was obtained between the ultrasonic response and the BIC. This QUS technique is more sensitive to changes of BII morphology compared to histological analyses.
Fichier principal
Vignette du fichier
Manon_SciRep.pdf (1.92 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03084516 , version 1 (21-12-2020)

Identifiants

Citer

Manon Fraulob, Romain Vayron, S. Le Cann, Benoît Lecuelle, Yoann Hériveaux, et al.. Quantitative ultrasound assessment of the influence of roughness and healing time on osseointegration phenomena. Scientific Reports, 2020, 10 (1), pp.1-12. ⟨10.1038/s41598-020-78806-0⟩. ⟨hal-03084516⟩
69 Consultations
61 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More