Impact of growth velocity on grain structure formation during directional solidification of a refined Al-20wt.%Cu alloy

Résumé

The paper presents detailed analyses of solidification experiments performed on a refined Al-20wt.%Cu alloy using the SFINX (Solidification Furnace with IN situ X-radiography) laboratory facility. Directional solidifications of a sheet-like sample were carried out in a horizontal configuration, with the main surface of the sample parallel to the ground. The sample was solidified for a wide range of cooling rates to obtain various grain structures, from columnar to elongated and equiaxed. The formation of the grain structure was observed in-situ and in real-time by X-radiography, which allows the dynamic of solidification phenomena to be thoroughly analyzed. Based on the radiographs, quantitative measurements were performed to
Fichier principal
Vignette du fichier
Soltani et al_2020-07-06.pdf (1.16 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03043701 , version 1 (07-12-2020)

Identifiants

Citer

H. Soltani, G. Reinhart, M.C. C Benoudia, F. Ngomesse, M. Zahzouh, et al.. Impact of growth velocity on grain structure formation during directional solidification of a refined Al-20wt.%Cu alloy. Journal of Crystal Growth, 2020, 548, pp.125819. ⟨10.1016/j.jcrysgro.2020.125819⟩. ⟨hal-03043701⟩
89 Consultations
288 Téléchargements

Altmetric

Partager

More