Transmission electron microscopy characterization of low temperature boron doped silicon epitaxial films

Résumé

Transmission electron microscopy (TEM) techniques can provide a complementary understanding of the physico-chemical mechanisms of the growth and the annealing behavior of boron-doped hydrogenated silicon epitaxial films grown at low temperatures (<200 °C) by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD). Compared to the standard boron diffusion or ion implantation, the PECVD process ensures a lower thermal budget and the realization of a sharper doping profile. The complexity of this epi-layer process lies on the fact that many impurities are incorporated during growth and their analysis requires the use of advanced characterization methods. Particular attention is paid to defects by combining high resolution transmission electron microscopy (HRTEM) and an image processing routine called geometric phase analysis (GPA) which allows the strain field to be studied. For the as-grown epitaxial layer, we will show how the non-conventional PECVD growth process influences its microstructure and gives it a non-uniform strain-field. In the annealed epitaxial layer, no strain is measured but nanotwins have been detected and analyzed through a geometric model. Scanning TEM (STEM) techniques are also applied to analyze chemical variation at the interface. A darker contrast is observed at the interface of the annealed sample most likely due to the migration of hydrogen atoms during annealing.

Domaines

Fichier principal
Vignette du fichier
Preprint CrystEngCom by G Noircler et al.pdf (1.39 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-03030275 , version 1 (14-12-2020)

Licence

Identifiants

Citer

Guillaume Noircler, Marta Chrostowski, Melvyn Larranaga, Etienne Drahi, Pere Roca I Cabarrocas, et al.. Transmission electron microscopy characterization of low temperature boron doped silicon epitaxial films. CrystEngComm, 2020, 22 (33), pp.5464-5472. ⟨10.1039/D0CE00817F⟩. ⟨hal-03030275⟩
335 Consultations
481 Téléchargements

Altmetric

Partager

  • More