Tuneable interplay between atomistic defects morphology and electrical properties of transparent p-type highly conductive off-stoichiometric Cu-Cr-O delafossite thin films - Archive ouverte HAL Access content directly
Journal Articles Scientific Reports Year : 2020

Tuneable interplay between atomistic defects morphology and electrical properties of transparent p-type highly conductive off-stoichiometric Cu-Cr-O delafossite thin films

Abstract

Off-stoichiometric copper chromium delafossites demonstrate the highest values of electric conductivity among the p-type transparent conducting oxides. Morphological and structural changes in cu 0.66 cr 1.33 o 2 upon annealing processes are investigated. chained copper vacancies were previously suggested as source of the high levels of doping in this material. High resolution Helium ion Microscopy, Secondary ion Mass Spectrometry and transmission electron Microscopy reveal a significant rearrangement of copper and chromium after the thermal treatments. Furthermore, positron Annihilation Spectroscopy evidences the presence of vacancy defects within the delafossite layers which can be assigned to the cu vacancy chains whose concentration decreases during the thermal process. These findings further confirm these chained vacancies as source of the p-type doping and suggest that the changes in electrical conductivities within the off-stoichiometric copper based delafossites are triggered by elemental rearrangements.
Fichier principal
Vignette du fichier
s41598-020-58312-z(1).pdf (2.31 Mo) Télécharger le fichier
Origin Publisher files allowed on an open archive

Dates and versions

hal-03026769 , version 1 (04-12-2020)

Identifiers

Cite

Petru Lunca-Popa, Jacques Botsoa, Mounib Bahri, Jonathan Crêpellière, Pierre Desgardin, et al.. Tuneable interplay between atomistic defects morphology and electrical properties of transparent p-type highly conductive off-stoichiometric Cu-Cr-O delafossite thin films. Scientific Reports, 2020, 10 (1), ⟨10.1038/s41598-020-58312-z⟩. ⟨hal-03026769⟩
65 View
21 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More