Influence of a Ceramic Substrate on Aqueous Precipitation and Structural Evolution of Alumina Nano-Crystalline Coatings - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of the American Ceramic Society Année : 2007

Influence of a Ceramic Substrate on Aqueous Precipitation and Structural Evolution of Alumina Nano-Crystalline Coatings

Résumé

Either boehmite (c-AlOOH) or gibbsite (c-Al(OH) 3) nanocrys-talline thin films (h% 100 nm) can be precipitated from AlCl 3 solution at fixed pH and temperature onto different substrates. It depends on the nature of the substrate (mica flakes, SiO 2 flakes, or a-Al 2 O 3 flakes), on their crystallographic properties (crystalline or amorphous), and on some experimental parameters (agitation rate, addition rate). According to the surface charge of the substrates, different alumina species are involved in the precipitation process. When negative charges are present on the substrate, the [Al 3 O(OH) 3 (OH 2) 9 ] 41 polycation is promoted , leading to the formation of the (Al 4) tetramer ([Al 4 O (OH) 10 (OH 2) 5 ] o) and then to the precipitation of bohemite. When positive charges are present, a ligand bridge containing complex ([Al 3 O(OH) 3 (O 2 H 3) 3 (OH 2) 9 ] 1) is likely favored, giving rise to hexagonal ring structures or amorphous solids that lead to the formation of gibbsite. Besides the surface effects, crystalline substrates can act as a template during precipitation of aluminum species as shown for the formation of gibbsite on muscovite. Finally, calcination at 8501C of boehmite samples leads to porous c-Al 2 O 3 layers, while calcination of gibbsite leads to d-Al 2 O 3 layers.

Domaines

Matériaux
Fichier principal
Vignette du fichier
2007-017.pdf (1.51 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02981072 , version 1 (27-10-2020)

Identifiants

Citer

Marie Mahé, Peter Reynders, Alain Demourgues, Jean-Marc Heintz. Influence of a Ceramic Substrate on Aqueous Precipitation and Structural Evolution of Alumina Nano-Crystalline Coatings. Journal of the American Ceramic Society, 2007, 90 (1), pp.217-224. ⟨10.1111/j.1551-2916.2006.01337.x⟩. ⟨hal-02981072⟩

Collections

CNRS ICMCB
50 Consultations
76 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More