Evaluation of electrochemical hydrogen absorption in welded pipe with steel API X52 - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue International Journal of Hydrogen Energy Année : 2013

Evaluation of electrochemical hydrogen absorption in welded pipe with steel API X52

I Dmytrakh
  • Fonction : Auteur
Z Azari
  • Fonction : Auteur
G Pluvinage

Résumé

Hydrogen charging of metal Cathodic polarisation Current density Hydrogen concentration Coefficient of efficiency of hydrogen permeation a b s t r a c t The assessment of ability to absorb hydrogen by welds components of API grade pipeline steel X52 has been done. The factors of cathodic hydrogen charging, time of exposure on hydrogen concentration in base metal, heat affected zone and metal of weld were taken into account. It has been shown that all components of weld demonstrate the sensitivity to hydrogenating in deoxygenated, near-neutral pH NS4 solution under relatively "soft" cathodic polarisation, although the efficiency of hydrogen permeation in metal is relatively low and depends on time of exposure. The ability to absorb hydrogen decreases in the following sequence: heat affected zone e base metal e weld. The sensitivity to hydroge-nation is higher for heat affected zone in comparison with base metal and weld.
Fichier non déposé

Dates et versions

hal-02972390 , version 1 (21-10-2020)

Identifiants

Citer

Julien Capelle, I Dmytrakh, Z Azari, G Pluvinage. Evaluation of electrochemical hydrogen absorption in welded pipe with steel API X52. International Journal of Hydrogen Energy, 2013, ⟨10.1016/j.ijhydene.2013.08.118⟩. ⟨hal-02972390⟩
7 Consultations
1 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More