Radical aqueous emulsion copolymerization of eugenol-derived monomers for adhesive applications - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Biomacromolecules Année : 2020

Radical aqueous emulsion copolymerization of eugenol-derived monomers for adhesive applications

Résumé

Biobased monomers derived from eugenol were copolymerized by emulsion polymerization to produce latexes for adhesive applications. Stable latexes containing ethoxy dihydroeugenyl methacrylate and ethoxy eugenyl methacrylate with high total solids content of 50 wt% were obtained and characterized. Latexes synthesis was carried out using a semi-batch process and latexes with particle diameters in the range of 159-178 nm were successfully obtained. Glass transition temperature values of the resulting polymers ranged between -32 and -28°C. Furthermore, tack and peel measurements confirmed the possibility to use these latexes in adhesive applications.

Domaines

Polymères
Fichier principal
Vignette du fichier
Revised Manuscript_PLD20200604_submitted.pdf (986.18 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02928837 , version 1 (02-09-2020)

Identifiants

Citer

Samantha Molina-Gutiérrez, W. S.Jennifer Li, Renaud Perrin, Vincent Ladmiral, Roberta Bongiovanni, et al.. Radical aqueous emulsion copolymerization of eugenol-derived monomers for adhesive applications. Biomacromolecules, 2020, 21, pp.4514-4521. ⟨10.1021/acs.biomac.0c00461⟩. ⟨hal-02928837⟩
103 Consultations
215 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More