Effect of hot isostatic pressing on the critical defect size distribution in AlSi7Mg0.6 alloy obtained by selective laser melting

Résumé

This study focuses on the influence of defect density on the sizes of the critical defects responsible for fatigue failure in AlSi7Mg0.6 alloy produced by Selective Laser Melting. Samples having similar microstructures and different defect densities were obtained combining Hot Isostatic Pressing and T6 treatments. Defect populations were analyzed using X-ray tomography, and fatigue tests were performed to determine the critical defect distributions. A method allowing for the prediction of these distributions from the CT scan data was then proposed, and discussed with regard to the actual distributions obtained from the fatigue tests.
Fichier principal
Vignette du fichier
I2M_IJF_BONNERIC_2020.pdf (1.9 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02924060 , version 1 (27-08-2020)

Identifiants

Citer

Matthieu Bonneric, Charles Brugger, Nicolas Saintier. Effect of hot isostatic pressing on the critical defect size distribution in AlSi7Mg0.6 alloy obtained by selective laser melting. International Journal of Fatigue, 2020, 140, pp.105797. ⟨10.1016/j.ijfatigue.2020.105797⟩. ⟨hal-02924060⟩
25 Consultations
83 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More