The Y–Mg–Co ternary system: alloys synthesis, phase diagram at 500 °C and crystal structure of the new compounds - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Alloys and Compounds Année : 2020

The Y–Mg–Co ternary system: alloys synthesis, phase diagram at 500 °C and crystal structure of the new compounds

V.V. Shtender
  • Fonction : Auteur
V.V. Pavlyuk
  • Fonction : Auteur
O.Ya Zelinska
  • Fonction : Auteur
W. Nitek
  • Fonction : Auteur
G.S. Dmytriv
  • Fonction : Auteur
W. Łasocha
  • Fonction : Auteur
I.Yu Zavaliy
  • Fonction : Auteur

Résumé

The ternary phase diagram of the Y-Mg-Co system have been studied at 500 °C by combining X-ray diffraction (XRD), energy dispersive X-ray (EDX) and wavelength dispersive X-ray (WDX). The existence of four ternary compounds Y4MgCo (Gd4RhIn-type), Y9Mg30Co2 (own structure type), Y6Mg9Co2 (own structure type) and Y9Mg4Co (Hf9Mo4B-type) was confirmed. For all of them homogeneity range has been defined. Two new ternary compounds were identified in this work: Y12MgCo5 (Ho12BiCo5-type, orthorhombic, Space Group Immm, a= 9.5078(5)-9.538(4) Å, b =9.4741(4)-9.531(4) Å, c = 10.0217(5)-10.061(5) Å) and ~Y52Mg3Co45 (unknown crystal structure). YCo3 and YCo2 compounds form extended solid solutions where maximum solubility of Mg is 8 and 16 at. %, respectively. The solubility of Mg in YCo2 leads to a structure change from MgCu2-type to SnMgCu4-type. It was also found that binary MgCo2 compound dissolve 4.9 at. % Y and YMg can dissolve up to 2.5 at. % of Co. New binary Y5Co6 compound was determined with two structures: a e low- and b e high-temperature. The a-Y5Co6 was indexed as monoclinic (a = 22.214 Å, b = 7.509 Å, c = 5.885 Å and b = 108.22°), while b-Y5Co6 crystalizes in the orthorhombic structure (space group Cmcm) with lattice parameters a = 4.104(1) Å, b = 10.246(1) Å and c = 20.336(3) Å. Detailed crystallographic data were collected for the Y5Mg0.07(1)Co5.93(1) and Y12MgCo5 single crystals. The metallic type bonding for Y12MgCo5 was confirmed by electronic structure calculations.
Fichier principal
Vignette du fichier
TbMgT4-H2_paper-HAL.pdf (1.96 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02921593 , version 1 (18-11-2020)

Identifiants

Citer

V.V. Shtender, V.V. Pavlyuk, O.Ya Zelinska, W. Nitek, V. Paul-Boncour, et al.. The Y–Mg–Co ternary system: alloys synthesis, phase diagram at 500 °C and crystal structure of the new compounds. Journal of Alloys and Compounds, 2020, 812, pp.152072. ⟨10.1016/j.jallcom.2019.152072⟩. ⟨hal-02921593⟩
34 Consultations
73 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More