Structure and optical properties of CrOxNy films with composition modulation

Résumé

The composition and structure properties of the CrOxNy films deposited by RF reactive magnetron sputtering were investigated and correlated with their optical properties. Two kinds of targets Cr2O3 and CrN compounds with variation of N2 and O2 gas flow were used to prepare two series of samples. The phase structure, chemical composition and optical properties of CrOxNy films were characterized by X-ray diffraction, X-ray photoelectron spectroscopy and ultraviolet-visible-near-infrared spectrophotometer, respectively. The films mainly consist of Cr2N and CrO3 phases. The Cr/ON ratio derived by XPS varies with the variation of nitrogen with Cr2O3 target. But only lower nitrogen content is detected with variation of oxygen using CrN target. TheCrOxNyy films with higher nitrogen content possess high absorbance around at 35% in the visible light range no matter the target.
Fichier principal
Vignette du fichier
Surf Eng.pdf (1.92 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02616495 , version 1 (24-05-2020)

Identifiants

Citer

Yanyan Yuan, Bingye Zhang, Jian Sun, Philippe Jonnard, Karine Le Guen, et al.. Structure and optical properties of CrOxNy films with composition modulation. Surface Engineering, 2020, 36 (4), pp.411-417. ⟨10.1080/02670844.2019.1656356⟩. ⟨hal-02616495⟩
113 Consultations
391 Téléchargements

Altmetric

Partager

More