The optical and light emission properties of tin and lead halide perovskites are remarkable because of the robust room-temperature (RT) performance, broad wavelength tunability, high efficiency, and good quenching resistance to defects. These highly desirable attributes promise to transform current light-emitting devices, phosphors, and lasers. One disadvantage in most of these materials is the sensitivity to moisture. Here, we report a new air-stable one-dimensional (1D) hybrid lead-free halide material (DAO)SnI (DAO, 1,8-octyldiammonium) that is resistant to water for more than 15 h. The material exhibits a sharp optical absorption edge at 2.70 eV and a strong broad orange light emission centered at 634 nm, with a full width at half-maximum (fwhm) of 142 nm (0.44 eV). The emission has a long photoluminescence (PL) lifetime of 582 ns, while the intensity is constant over a very broad temperature range (145-415 K) with a photoluminescence quantum yield (PLQY) of at least 20.3% at RT. Above 415 K the material undergoes a structural phase transition from monoclinic (2/) to orthorhombic ( accompanied by a red shift in the band gap and a quench in the photoluminescence emission. Density functional theory calculations support the trend in the optical properties and the 1D electronic nature of the structure, where the calculated carrier effective masses along the inorganic chain are significantly lower than those perpendicular to the chain. Thin films of the compound readily fabricated from solutions exhibit the same optical properties, but with improved PLQY of 36%, for a 60 nm thick film, among the highest reported for lead-free low-dimensional 2D and 1D perovskites and metal halides.