Contact plastic accommodation influence on the fretting fatigue cracking response of steel
Influence de l'accommodation plastique du contact sur la fissuration d'un acier soumis à des sollicitations de fretting fatigue
Résumé
This works aim to quantify safe running fretting-fatigue condition for a severely plastic contact by predicting the crack nucleation condition. Experimental results show that the crack nucleation condition is stable despite increasing fatigue loading. Yet, the fatigue stress tends to increase the global stressing so that the related threshold fretting contact stressing is expected to be reduced. Simulations have been done and the crack nucleation condition was addressed by transposing the Crossland's multiaxial fatigue criterion at a critical distance to take into account the contact stress gradient. Contact plastic accommodation phenomenon is shown to explain the plateau evolution of the crack nucleation condition.
Ce travail a pour but de dimensionner la réponse en fretting-fatigue d'un contact sévèrement déformé plastiquement en prédisant la condition d'amorçage de fissure. Des essais expérimentaux montrent que la condition d'amorçage en fretting (force tangentielle) est stable malgré l'augmentation du chargement de fatigue. Or une augmentation de la sollicitation de fatigue est sensée augmenter le chargement global de sorte que la valeur seuil du chargement de fretting devrait être diminuée. Des simulations ont été réalisées, et la condition d'amorçage calculée en utilisant le critère de Crossland à une distance critique afin de prendre en compte les gradients de contrainte. L'accommodation plastique du contact apparait être à l'origine de l'évolution en plateau de la condition d'amorçage.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|