Contact resistivity of Al/Ti ohmic contacts on p-type ion implanted 4H and 6H-SiC

Résumé

Al-Ti alloys with 72 wt% Al were employed for the realisation of ohmic contacts on 4E19 cm-3 p-type ion implanted 4H- and 6H-SiC samples. Contact resistivity characterisations by TLM measurements were done at wafer level in the temperature range 28-290°C. Analysis of the TLM measurements took into account current crowding at the metal pads. More than half of the evaluated contact resistivity reached the minimum value detectable by the used TLM devices, that was slightly higher than 1E-6 ohm.cm2. Above this limit value, contact resistivity decreased for increasing temperature and was spread over a few decades. The maximum contact resistivity at 28°C was 2E-4 ohm.cm2, which changed to 5E-6 ohm.cm2 at 290°C. The thermal behaviour of these TLM structures featured thermionic-field emission conduction.
Fichier principal
Vignette du fichier
metalli_32.pdf (240.23 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02485106 , version 1 (19-02-2020)

Identifiants

Citer

Roberta Nipoti, Francesco Moscatelli, Andrea Scorzoni, Antonella Poggi, Gian Carlo Cardinali, et al.. Contact resistivity of Al/Ti ohmic contacts on p-type ion implanted 4H and 6H-SiC. 2002 MRS Fall Meeting, Dec 2002, Boston, United States. ⟨10.1557/PROC-742-K6.2⟩. ⟨hal-02485106⟩
54 Consultations
216 Téléchargements

Altmetric

Partager

More