Increase of magnetic and magnetoelectric properties in Co/Mn co-doped BiFeO3 multiferroic

Résumé

Co and Mn co-doped BiFeO3 samples are successfully realized using a stirred hydrothermal route to form BiFe0.9CoxMn0.1-xO3 (for x=0.01, 0.03, 0.05, 0.07 and 0.09) system. Our data show that both the ferroelectric (TC) and antiferromagnetic (TN) transition temperatures increase especially TN varies by up to 23°C when changing from BiFe0.9Co0.01Mn0.09O3 to BiFe0.9Co0.09Mn0.01O3. Such strong TN enhancement is explained by Co ionic size which induces a chemical pressure by reducing the unit cell and consequently favor the exchange coupling between the magnetic moments carried by Fe/Co/Mn. Moreover, Co 3+ (d 6 electronic configuration) by replacing Fe (d 5) increases the magnetization reaching a value of 3.394 emu/g for BiFe0.9Co0.09Mn0.01O3, by favoring double exchange interactions. The direct magnetoelectric (ME) measurements on those samples show a significant increase of the ME coefficient with a value of 8.720 mV/(Oe.cm) for BiFe0.9Co0.05Mn0.05O3 i.e. up to 6 times higher than that of pure BiFeO3. For Mn-rich compositions, because of a parasitic Bi25FeO40 phase and high electric losses, no intrinsic ME coefficient could be measured.
Fichier principal
Vignette du fichier
20_03_brahim_4.pdf (648.51 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02483201 , version 1 (18-02-2020)

Identifiants

Citer

Arij Marzouki, Vincent Loyau, Pascale Gemeiner, Lotfi Bessais, Brahim Dkhil, et al.. Increase of magnetic and magnetoelectric properties in Co/Mn co-doped BiFeO3 multiferroic. Journal of Magnetism and Magnetic Materials, 2020, 498, pp.166137. ⟨10.1016/j.jmmm.2019.166137⟩. ⟨hal-02483201⟩
108 Consultations
158 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More