Study of the surface oxides and corrosion behaviour of an equiatomic CoCrFeMnNi high entropy alloy by XPS and ToF-SIMS - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Corrosion Science Année : 2020

Study of the surface oxides and corrosion behaviour of an equiatomic CoCrFeMnNi high entropy alloy by XPS and ToF-SIMS

Résumé

XPS and ToF-SIMS analysis have been combined with electrochemical measurements to determine the corrosion behavior of the equiatomic CoCrFeMnNi high entropy alloy. An XPS methodology based on analysis of the 3p core level spectra was developed to determine the composition and thickness of oxide films. Both native oxide (∼1.4nm) and passive films (∼ 1.6nm) formed in acidic medium are duplex, comprising Cr and Mn inner layer and Cr/Fe/Co mixture outer layer. No nickel is observed in the oxide layer. The effects of exposure of the native film to sulfuric acid and passivation under anodic polarization have been investigated.
Fichier principal
Vignette du fichier
CIMNAS Article 15_Preprint.pdf (1023.58 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02470246 , version 1 (07-02-2020)

Identifiants

Citer

Luntao Wang, Dimitri Mercier, Sandrine Zanna, Antoine Seyeux, Mathilde Laurent-Brocq, et al.. Study of the surface oxides and corrosion behaviour of an equiatomic CoCrFeMnNi high entropy alloy by XPS and ToF-SIMS. Corrosion Science, 2020, 167, pp.108507. ⟨10.1016/j.corsci.2020.108507⟩. ⟨hal-02470246⟩
189 Consultations
482 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More