Al-rich Fe0.85 Al0.15 (100), (110) and (111) surface structures


Based on previous photoemission findings, the influence of newly observed aluminum surface segregation at the low (110), (100) and (111) index surfaces of the A 2 body-centered Fe 0.85 Al 0.15 random alloy is explored. Scanning Tun-neling Microscopy, Low-Energy Electron Diffraction and Grazing-Incidence X-Ray Diffraction are combined to explore surface structures and topogra-phies. The formation of a surface composition close to the B 2 Fe 0.5 Al 0.5 occurs with the appearance of (i) a long-range pseudo-hexagonal incommen-surate superstructure with a periodicity of ∼ 18Å on the (110) surface, (ii) a (1 × 1) termination on the (100) surface and (iii) a intense vicinal faceting of the (111) surface in the form of triangular pits.
Fichier principal
Vignette du fichier
FeAl_surface_structure_v8.pdf (2.69 Mo) Télécharger le fichier
FeAl_surface_structure_SI_1.pdf (6.24 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-02451294 , version 1 (27-01-2020)



Zongbei Dai, Natalia Alyabyeva, Patrizia Borghetti, Stéphane Chenot, Pascal David, et al.. Al-rich Fe0.85 Al0.15 (100), (110) and (111) surface structures. Applied Surface Science, 2020, 509, pp.145312. ⟨10.1016/j.apsusc.2020.145312⟩. ⟨hal-02451294⟩
106 View
62 Download



Gmail Facebook X LinkedIn More