Defects and damages detection in thick PMC
Détection de défauts et endommagements dans des CMO épais
Résumé
For lifetime extension of wind turbine blades, it appears mandatory to rely on non-destructive testing for blade inspection. Wind turbine blades (PMC) are characterized by their high thickness, what makes common techniques unsuitable for their inspectionin operational conditions. Hence, EDF R&D studied the capability of dielectric permittivity-based techniques to detect heterogeneities in samples representative of blades, both sound and with calibrated defects. Permittivity measurements were performed using coaxial probes and radars, on both monolithic and sandwich composites. The results showed that this physical value is suitable for defects and damages detectio
Dans l’objectif d’allonger la durée de vie des pales d’éoliennes, il s’avère aujourd’hui nécessaire d’avoir recours à des inspections reposant sur du contrôle non-destructif. Les pales d’éoliennes (CMO) présentant la particularité d’être épaisses, les techniques d’inspection classiques ne sont pas adaptées à des inspections en conditions opérationnelles. Ainsi, EDF R&D a étudié la possibilité de détecter des hétérogénéités à partir de mesure de permittivité diélectrique sur des éprouvettes représentatives de pales d’éoliennes, saines et avec défauts calibrés. Les mesures de permittivité réalisées par sonde coaxiale et par radar, sur des éprouvettes en composites monolithique et sandwich, ont montré que cette grandeur physique est adaptée à la détection de défauts et endommagements.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|
Loading...