Interface formation versus fibres properties: effects on mechanical behaviour of bio-based composites manufactured by infusion
Effet de la formation de l'interface et des propriétés des fibres dans le comportement mécanique de composites bio-sourcés fabriqués par infusion
Résumé
The aim is to study the effect of the modification of the free surface energy of flax fibres by a thermal treatment on the mechanical behaviour of bio-based composites. It has been proved that this modification enhancesthe wettability of flax fibers by epoxy resin and resultsin a lower porosity amount in composites. Tests to evaluate mechanical properties of elementary fibres, yarns and composites have been performed. The main conclusion is that, even if elementary fibres and yarns have been embrittled and work of adhesion hasbeen lowered after thermal treatment, since the wettability of fibers has been improved, the mechanical behaviour of composites manufactured by LCM is better with treated fibers.
Le but de la présente étude est de prouver l’effet d’une modification d’énergie de surface de fibres de lin par traitement thermique sur le comportement mécanique de composites bio-sourcés. Il a été montré que ce traitement améliore le mouillage des fibres par de la résine époxy en réduisant le taux de porosité dans le composite. Des tests visant à évaluer les propriétés mécaniques des fibres élémentaires, des fils et du composite ont été menés. La conclusion est que, même si les fibres élémentaires et les fils ont été fragilisés et que le travail d’adhésion a diminué, comme le mouillage a été amélioré, le comportement mécanique des composites renforcés par des fibres traitées, élaborée par infusion, est meilleur.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|
Loading...