Optically active Er3+ ions in SiO2 codoped with Si nanoclusters
Résumé
Optical properties of directly excited erbium (Er3+) ions have been studied in silicon rich silicon oxide materials codoped with Er3+. The spectral dependence of the direct excitation cross section (σdir) of the Er3+ atomic 4I152→4I112 transition (around 0.98 μm) has been measured by time resolved µ-photoluminescence measurements. We have determined that σdir is 9.0±1.5 x10−21 cm2 at 983 nm, at least twice larger than the value determined on a stoichiometric SiO2 matrix. This result, in combination with a measurement of the population of excited Er3+ as a function of the pumping flux, has allowed quantifying accurately the amount of optically active Er3+. This concentration is, in the best of the cases, 26% of the total Er population measured by secondary ion mass spectrometry, which means that only this percentage could provide optical gain in an eventual optical amplifier based on this material.
Domaines
Optique / photoniqueOrigine | Fichiers éditeurs autorisés sur une archive ouverte |
---|
Loading...