About thermo-oxidative ageing at moderate temperature of conventionally vulcanized natural rubber

Résumé

This article is dedicated to the understanding of the mechanisms involved in the evolution of the structure of a “conventionally” vulcanized rubber during thermo-oxidative (TO) aging. Based on swelling measurements, WAXS and DSC, a scenario of these mechanisms is proposed. Our results show that the crosslinking reactions are far from being complete at the end of the vulcanization process. During TO aging carried out at a moderate temperature 77 °C (350 K), the creation of long bridges first takes place via the consumption of residual sulfur; this mechanism is mainly responsible of the increase in the density of elastically active chains. The presence of residual antioxidants inhibits in the early stages of aging the chemical reactions involving oxygen. For longer aging time (here 7 days), these reactions can then occur and create “unidentified” bridges whose formation may also involves sulfur grafted onto the polymer chains. Finally, all these cross-linking reactions seem to enhance the heterogeneity of the spatial distribution of the crosslinks - already existing in the initial material - and to create highly crosslinked domains. © 2018
Fichier principal
Vignette du fichier
S0141391018304154.pdf (1.71 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02405462 , version 1 (21-10-2021)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

F. Grasland, L. Chazeau, J.-M. Chenal, R. Schach. About thermo-oxidative ageing at moderate temperature of conventionally vulcanized natural rubber. Polymer Degradation and Stability, 2019, 161, pp.74-84. ⟨10.1016/j.polymdegradstab.2018.12.029⟩. ⟨hal-02405462⟩
77 Consultations
282 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More