Aligned High Density Semi‐Conductive Ultra‐Small Single‐Walled Carbon Nanotubes

Yun Wang
  • Fonction : Auteur
  • PersonId : 759448
  • IdRef : 117267732
Teng Ben
  • Fonction : Auteur
Shilun Qiu
  • Fonction : Auteur

Résumé

Zeolite type material (AlPO‐5, AFI‐type) with rod‐like morphology and mono‐dimensional channel system running along the long crystal axis was vertically grown on a stainless‐steel plate. The organic template used in the synthesis was carbonized to generate single‐walled carbon nanotubes (SWCNTs). Thus, SWCNTs with a diameter of 0.4 nm, perfectly aligned and vertically oriented to the support surface with a density of 2.6 × 105 SWCNTs μm−2, were obtained. The free end of AlPO‐5 crystal was chemically etched in order to create contact surface and measure the conductivity of SWCNT@AlPO‐5 film which was found to be 4.16 × 10−1 Ω−1 cm−1. This approach of aligned SWCNTs can be applied to different types of substrates, thus opening the road to practical uses of SWCNTs.

Domaines

Matériaux
Fichier principal
Vignette du fichier
10.1002slct.201904178 corrected.pdf (350.59 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03033927 , version 1 (17-12-2020)

Identifiants

Citer

Yun Wang, Teng Ben, Shilun Qiu, Valentin Valtchev. Aligned High Density Semi‐Conductive Ultra‐Small Single‐Walled Carbon Nanotubes. ChemistrySelect, 2019, 4 (43), pp.12676-12679. ⟨10.1002/slct.201904178⟩. ⟨hal-03033927⟩
29 Consultations
114 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More