Investigation of OSN properties of PDMS membrane for the retention of dilute solutes with potential industrial applications

Résumé

Few commercially available membranes can be used for organic solvent nanofiltration (OSN). Applying OSN in chemical industries is nevertheless of high interest to cut with energy consumption linked to solvent recycling and soluble catalysts recovery. A commercial membrane, PERVAP4060, was used to investigate the retention of dilute solutes in toluene feeds and to mimic metathesis medium. The studied solutes were R-BINAP a neutral polyaromatic molecule used in metathesis chemistry, tetraoctylammonium bromide (ToABr), a charged molecule used as a homogeneous catalyst and n-hexadecane. Retention of polar ToABr (95%) was higher than that of neutral R-BINAP (80%). The transfer mechanism, either pore flow or solution-diffusion, was discussed. All the results obtained suggested that the transport is governed by the solution-diffusion mechanism. The measured retentions could be explained in terms of solubility affinities and diffusion coefficients. The stability and performances of PERVAP4060 were well established, showing the strong potential for industrial applications.
Fichier principal
Vignette du fichier
JAPS-Morshed-PDMS rev.app.2019.pdf (2.25 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02391534 , version 1 (04-12-2019)

Identifiants

Citer

Mahbub Morshed, Herve Simonaire, Halima Alem, Denis Roizard. Investigation of OSN properties of PDMS membrane for the retention of dilute solutes with potential industrial applications. Journal of Applied Polymer Science, 2020, 137 (6), pp.48359. ⟨10.1002/app.48359⟩. ⟨hal-02391534⟩
139 Consultations
186 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More