Cr cluster characterization in Cu-Cr-Zr alloy after ECAP processing and aging using SANS and HAADF-STEM - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Kovové materiály [Metallic materials] Année : 2019

Cr cluster characterization in Cu-Cr-Zr alloy after ECAP processing and aging using SANS and HAADF-STEM

K. Abib
  • Fonction : Auteur
H. Azzeddine
  • Fonction : Auteur
B. Alili
  • Fonction : Auteur
L. Litynska-Dobrzynska
  • Fonction : Auteur
M. Mathon
P. Zieba
  • Fonction : Auteur
D. Bradai
  • Fonction : Auteur

Résumé

The precipitation of nano-sized Cr clusters was investigated in a commercial Cu-1Cr-0.1Zr (wt.%) alloy processed by Equal-Channel Angular Pressing (ECAP) and subsequent aging at 550 °C for 4 hours using small angle neutron scattering (SANS) measurements and high-angle annular dark-field-scanning transmission electron microscopy (HAADF-STEM). The size and volume fraction of nano-sized Cr clusters were estimated using both techniques. These parameters assessed from SANS (d~3.2 nm, Fv~1.1 %) agreed reasonably with those from HAADF-STEM (d ~2.5 nm, Fv~2.3%). Besides nano-sized Cr clusters, HAADF-STEM technique evidenced the presence of rare cuboid and spheroid sub-micronic Cr particles about 380-620 nm mean size. Both techniques did not evidence the presence of intermetallic CuxZry phases within the aging conditions.
Fichier principal
Vignette du fichier
Abib et al. 2019.pdf (794.91 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02360002 , version 1 (11-12-2019)

Identifiants

Citer

K. Abib, H. Azzeddine, B. Alili, L. Litynska-Dobrzynska, A. Helbert, et al.. Cr cluster characterization in Cu-Cr-Zr alloy after ECAP processing and aging using SANS and HAADF-STEM. Kovové materiály [Metallic materials], 2019, 57 (02), pp.121-129. ⟨10.4149/km_2019_1_121⟩. ⟨hal-02360002⟩
78 Consultations
78 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More