Selective laser melting of tungsten carbide reinforced maraging steel composite

Résumé

In this work, tungsten carbide (WC) reinforced maraging steel matrix composites were in-situ manufactured by selective laser melting (SLM) from powder mixture. The SLM processed samples presented high relative density (over 99%) with a homogenous distribution of WC. The as-fabricated surface quality of SLM processed samples was improved significantly by the addition of WC. Focused ion beam and transmission electron microscopy were employed to characterize the interfacial properties between tungsten carbide and steel matrix. The elemental analysis indicates that metallurgical bonding appears at interfacial region due to the diffusion. Tensile behavior of SLM processed maraging steel was different from their composite with several WC contents.

Domaines

Matériaux
Fichier principal
Vignette du fichier
M2P_ADDITIVE MANUFACTURING_HERAUD_2018.pdf (2.57 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02355643 , version 1 (16-09-2020)

Identifiants

Citer

Nan Kang, Wenyou Ma, Lorene Heraud, Mohamed El Mansori, Fuhai Li, et al.. Selective laser melting of tungsten carbide reinforced maraging steel composite. Additive Manufacturing, 2018, 22, pp.104-110. ⟨10.1016/j.addma.2018.04.031⟩. ⟨hal-02355643⟩
70 Consultations
256 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More