Superconductivity at 80 K in (Sr,Ca)3Cu2O4+δCl2-y induced by apical oxygen doping - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Nature Année : 1995

Superconductivity at 80 K in (Sr,Ca)3Cu2O4+δCl2-y induced by apical oxygen doping

C. -Q. Jin
  • Fonction : Auteur
X. -J. Wu
  • Fonction : Auteur
P. Laffez
T. Tatsuki
  • Fonction : Auteur
T. Tamura
  • Fonction : Auteur
S. Adachi
  • Fonction : Auteur
H. Yamauchi
  • Fonction : Auteur
N. Koshizuka
  • Fonction : Auteur
S. Tanaka
  • Fonction : Auteur

Résumé

RECENT work has shown that superconducting copper oxyhalides can be synthesized, with the La2CuO4structure but with no oxygen in the ‘apical’ positions outside the CuO2 planes. For these materials to be rendered superconducting, charge carriers must be introduced into the CuO2 planes; in previous work, positive carriers (holes) have been introduced by the incorporation of interstitial fluorine in Sr2CuO2F2+δ (transition temperature Tc = 46 K)1, or by the substitution of sodium for calcium in (Ca,Na)2CuO2Cl2 (Tc = 26 K)2. Here we present an alternative doping approach for this copper oxyhalide family: holes are introduced by partially replacing the (monovalent) halogen that occupies the apical sites with (divalent) oxygen. We have obtained bulk superconductivity with Tc above 77 K in a new double-layer compound (Sr,Ca)3Cu2O4+δCl2-y, which is isostructural with (La,Sr)2-CaCu2O6 (ref. 3), with (Sr,Ca) at the (La,Sr) or Ca sites, and Cl at the apical sites outside the CuO2 planes.

Domaines

Matériaux
Fichier principal
Vignette du fichier
375301a0.pdf (5.39 Mo) Télécharger le fichier
Origine : Accord explicite pour ce dépôt
Loading...

Dates et versions

hal-02349838 , version 1 (05-11-2019)

Identifiants

Citer

C. -Q. Jin, X. -J. Wu, P. Laffez, T. Tatsuki, T. Tamura, et al.. Superconductivity at 80 K in (Sr,Ca)3Cu2O4+δCl2-y induced by apical oxygen doping. Nature, 1995, 375, pp.301-303. ⟨10.1038/375301a0⟩. ⟨hal-02349838⟩

Collections

CNRS UNIV-LEMANS
12 Consultations
64 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More