An X-ray powder diffraction study of damage produced in Ca(OH)2 and Mg(OH)2 by electron irradiation using the 2.5 MeV SIRIUS accelerator - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Nuclear Materials Année : 2018

An X-ray powder diffraction study of damage produced in Ca(OH)2 and Mg(OH)2 by electron irradiation using the 2.5 MeV SIRIUS accelerator

Résumé

Two isomorphous hydrous minerals, Mg(OH)2 and Ca(OH)2, were exposed to the 2.5 MeV electron beam of the SIRIUS accelerator platform. Both compounds remain stable under the beam up to high doses, in the range of 3–3.5 GGy. No decomposition is observed. But contrary to earlier statements, a net difference of reactivity between them is highlighted as a result of the present X-ray powder diffraction study: i) a significant dilatation is observed along the c - axis, more significant in brucite than in portlandite as already reported during thermal decomposition studies, ii) but a contraction is here revealed in the basal plane of brucite, along the a – axis, while a slight dilatation is still being observed in portlandite. Contraction in the basal plane seems a specific feature of electron irradiation only once previously observed by TEM in brucite. Moreover for brucite, the decreasing intensities of Bragg lines together with the appearance of a diffuse scattering over the whole angular range is compatible with the appearance of some static structural disorder induced by electron irradiation. Finally electron irradiation leads to a significant reduction in crystallite size with increasing dose, by a factor of 2 at the intermediate dose of 310 MGy in brucite, while for a comparable effect to occur an absorbed dose of 3.5 GGy should be attained in portlandite.

Domaines

Cristallographie
Fichier principal
Vignette du fichier
HAL_de Noirfontaine et al._JNM_2018.pdf (1.48 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02301326 , version 1 (15-07-2021)

Identifiants

Citer

Marie-Noëlle de Noirfontaine, Loren Acher, Mireille Courtial, Frederic Dunstetter, Dominique Gorse-Pomonti. An X-ray powder diffraction study of damage produced in Ca(OH)2 and Mg(OH)2 by electron irradiation using the 2.5 MeV SIRIUS accelerator. Journal of Nuclear Materials, 2018, 509, pp.78-93. ⟨10.1016/j.jnucmat.2018.06.019⟩. ⟨hal-02301326⟩
81 Consultations
75 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More