Development of a kinetic model for the moderate temperature chemical vapor deposition of SiO2 films from tetraethyl orthosilicate and oxygen - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue AIChE Journal Année : 2018

Development of a kinetic model for the moderate temperature chemical vapor deposition of SiO2 films from tetraethyl orthosilicate and oxygen

Résumé

An apparent kinetic model for the chemical vapor deposition of SiO2 from tetraethyl orthosilicate (TEOS) and O2 was developed in a poorly investigated range of operating conditions, that is, at atmospheric pressure and between 350 and 500°C, based on literature survey and experimental results obtained in a hot wall tubular reactor. The kinetic model was implemented into the computational fluid dynamics code FLUENT and validated both in shape and value by comparison with experimental deposition rate profiles. It reveals th at for the conditions tested, a possible mechanism of SiO2 deposition involves two intermediate species formed from TEOS homogeneous decomposition, the first one being active from 300°C and the second one contributing to deposition for temperatures higher than 370°C. The calculated local profiles of gas flow, gas temperature, species mass fraction, and silica deposition rate indicate that the first intermediate species leads to marked film thickness gradients, the second one being more stable as producing uniform thicknesses.
Fichier principal
Vignette du fichier
Ponton_20815.pdf (1.05 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02134788 , version 1 (20-05-2019)

Identifiants

Citer

Simon Ponton, Hugues Vergnes, Diane Samélor, Daniel Sadowski, Constantin Vahlas, et al.. Development of a kinetic model for the moderate temperature chemical vapor deposition of SiO2 films from tetraethyl orthosilicate and oxygen. AIChE Journal, 2018, 00, pp.1-9. ⟨10.1002/aic.16222⟩. ⟨hal-02134788⟩
60 Consultations
500 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More