Influence of viscosity for oil-in-water and water-in-oil nanoemulsions production by SPG premix membrane emulsification

Résumé

Oil-in-water and water-in-oil nanoemulsions are interesting carriers for respectively oil soluble and water soluble actives. In this study, oil-in-water (O/W) and water-in-oil (W/O) nanoemulsions were prepared by premix membrane emulsification. A coarse emulsion (premix) was injected thanks to a high pressure pump through a Shirasu Porous Glass (SPG) membrane with pore size of 0.5 µm in order to reduce and homogenize the droplet size. The effect of viscosities on the pressure and droplet size was investigated: the water phase viscosity by increasing glycerol concentration, the oil phase viscosity with mineral oils of different viscosities and the overall emulsion viscosity by increasing the dispersed phase content of the emulsion. The pressure required to break up the droplets inside the membrane pores ∆P dis did not depend on viscosities, while the pressures generated by the flows through the pipe ∆P pipe and the membrane ∆P f low were proportional to the viscosity of the overall emulsion. W/O nanoemulsions were more difficult to produce and to characterize but thanks to the original setup working at pressures up to 65 bar and high flowrates, W/O mineral oil nanoemulsions were produced with mean droplets size around 600 nm and flow rate of 50 mL/min.
Fichier principal
Vignette du fichier
Alliod_et_al_2018b.pdf (5.51 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02096957 , version 1 (03-06-2019)

Identifiants

Citer

Océane Alliod, Léa Messager, Hatem Fessi, Damien Dupin, Catherine Charcosset. Influence of viscosity for oil-in-water and water-in-oil nanoemulsions production by SPG premix membrane emulsification. Chemical Engineering Research and Design, 2019, 142, pp.87-99. ⟨10.1016/j.cherd.2018.11.027⟩. ⟨hal-02096957⟩
62 Consultations
901 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More